Sikaflex® P2G Premium
Sikaflex® P2G Premium is a cold-applied, fast curing, high-viscosity polyurethane adhesive designed for use in replacing direct glazed automotive glass parts. Sikaflex® P2G Premium does not require the use of a Sika® Aktivator or Sika® Primer pre-treatment product on glass or ceramic frit. When used as directed Sikaflex® P2G Premium is an appropriate adhesive for use in auto glass replacement applications.
- Primerless to glass adhesion
- 3 hour Minimum Drive Away Time (MDAT); tested according to FMVSS 212
- Can be used for non-conductive applications
- Can be used from 4 – 43 °C
PRODUCT BENEFITS
- Primerless to glass adhesion
- 3 hour Minimum Drive Away Time (MDAT); tested according to FMVSS 212
- Can be used for non-conductive applications
- Can be used from 4 – 43 °C
Usage
This product is suitable for experienced professional users only.This product and related process information is designed for Automotive Glass Replacement. For other applications, tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.
Packaging
| Cartridge | 300 ml |
| Unipack | 600 ml |
Product Details
| Chemical base | 1-component polyurethane | |
| Color (CQP001-1) | Black | |
| Cure mechanism | Moisture-curing | |
| Density (uncured) | 1.1 kg/l | |
| Non-sag properties | Very good | |
| Application temperature | product ambient substrate | 10 – 35 °C (50 – 95 °F) 4 – 43 °C (40 – 110 °F) 4 – 54 °C (40 – 130 °F) |
| Skin time (CQP019-1) | 35 minutes A | |
| Open time (CQP526-1) | 15 minutes A | |
| Shore A hardness (CQP023-1 / ISO 48-4) | 65 | |
| Tensile strength (CQP036-1 / ISO 527) | 6.5 MPa (940 psi) | |
| Elongation at break (CQP036-1 / ISO 527) | 600 % | |
| Tensile lap-shear strength (CQP046-1 / ISO 4587) | 5.0 MPa (720 psi) | |
| Minimum Drive Away Time (cars) according FMVSS 212 (CQP511-1) | 3 hours | |
| Service temperature (CQP509-1 / CQP513-1) | -40 – 93 °C (-40 – 200 °F) | |
| Shelf life | 9 months B |
| CQP = Corporate Quality Procedure | A) 23 °C (73 °F) / 50 % r.h. | B) stored below 25 °C (77 °F) |
CURE MECHANISM
Sikaflex® P2G Premium cures by reaction with atmospheric moisture. At low temperatures the water content of the air is generally lower and the curing reaction proceeds somewhat slower. For the Minimum Drive Away Time please see the table on page 1.
CHEMICAL RESISTANCE
Sikaflex® P2G Premium is generally resistant to fresh water, seawater, diluted acids and diluted caustic solutions; temporarily resistant to fuels, mineral oils, vegetable and animal fats and oils; not resistant to organic acids, glycolic alcohol, concentrated mineral acids and caustic solutions or solvents.
Application
Surface Preparation
Surfaces must be clean, dry and free from grease, oil, dust and contaminants.
The bond faces must be prepared with an Automotive grade glass cleaner. Sikaflex® P2G Premium is capable to bond on glass and ceramic frits without additional pre-treatment. Further information on the application and use of cleaning agent, can be found in the corresponding Product Data Sheet.
All corrosion must be removed and all bare metal scrapes and scratches must be prepared in accordance with Sika's Corrosion Treatment recommendations. For preparation of all bonding surfaces it is required to read and understand the instructions given in Sika's General Guideline for Vehicle Glass Replacement (formerly Sika AGR Technician Training Manual).
Windshields without ceramic coating need proper UV protection.
Application
It is recommended to apply Sikaflex® P2G Premium with a powerful battery operated application gun.
Consider that the viscosity will increase at low temperature. For easy application, condition the adhesive at ambient temperature prior to use.
To ensure a uniform thickness of the bondline it is recommended to apply the adhesive in form of a triangular bead (see figure 1).
Figure 1: Recommended bead configuration
The open time is significantly shorter in hot and humid climate. The glass must always be installed within the open time. Never install a glass after the adhesive has built a skin.
Removal
Uncured Sikaflex® P2G Premium may be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes or a suitable industrial hand cleaner and water.
Do not use solvents on skin.