Sikasil® WT-488
0.0 (0)
Sikasil® WT-488 is a two-part, non-corrosive, fast-curing silicone sealant and adhesive for structural bonding of insulating glass units into window frames and for back-bedding applications.
- Meets the requirements of AMAA 802.3 and AMAA 805.2
- Designed for adhesion to a wide variety of substrates
- Very good mechanical properties for window bonding applications
- Superior UV and weathering resistance
- Remains flexible over a wide temperature range
- Long-term durability
PRODUCT BENEFITS
- Meets the requirements of AMAA 802.3 and AMAA 805.2
- Designed for adhesion to a wide variety of substrates
- Very good mechanical properties for window bonding applications
- Superior UV and weathering resistance
- Remains flexible over a wide temperature range
- Long-term durability
Usage
Sikasil® WT-488 has a wide adhesion range on many substrates such as glass, (coated) metal, wood, PVC and many other substrates. In combination with its good mechanical properties, this makes the adhesive suitable for structural bonding of insulating glass units into window frames and for back-bedding applications. It is further suitable for demanding industrial bonding and sealing applications. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.Packaging
Sikasil® WT-488 (A)
| Drum | 260 kg |
Sikasil® AS-785 (B)
| Pail | 20 kg |
Product Details
| Properties |
| ||||
| Chemical base | 2-component silicone | ||||
| Color (CQP001-1) |
|
| |||
| Cure mechanism | Polycondensation | ||||
| Cure type | Alkoxy | ||||
| Density (uncured) |
|
| |||
| Mixing ratio | A:B by volume A:B by weight | 10:1 12:1 | |||
| Viscosity (CQP029-5 / ISO 3219) |
| ||||
| Consistency | Paste | ||||
| Application temperature | 5 ─ 40 °C (41 ─ 104 °F) | ||||
| Snap time (CQP554-1) | 10 minutes A | ||||
| Tack free time (CQP019-3) | 40 minutes A | ||||
| Shore A hardness (CQP023-1 / ISO 48-4) | 35 | ||||
| Tensile strength (CQP036-1 / ISO 527) | 2.0 MPa (290 psi) | ||||
| 100 % modulus (CQP036-1 / ISO 527) | 0.6 MPa (85 psi) | ||||
| Elongation at break (ASTM D412) | 300 % | ||||
| Service temperature (CQP513-1) | -40 ─ 150 °C (-40 ─ 302 °F) | ||||
| Shelf life |
|
| CQP = Corporate Quality Procedure | A) 23 °C (73 °F) / 50 % r. h. | B) stored below 25 °C (77 °F) |
CURE MECHANISM
Sikasil® WT-488 starts to cure immediately after mixing the 2-components.
The speed of the reaction depends mainly on the temperature, i.e. the higher the temperature the faster the curing process. Do not heat above 50 °C (122 °F), as this could lead to bubble formation.
The mixer open time, i. e. the time the material can remain in the mixer without flushing or extrusion of product, is significantly shorter than the snap time indicated above.
Application
METHOD OF APPLICATION
Surface Preparation
Surfaces must be clean, dry and free from grease, oil and dust. Surface treatment depends on the specific nature of the substrates and is crucial for a long lasting bond.
Application
The optimum temperature for substrate and process material is between 15 °C and 25 °C (59 °F and 77 °F).
Before processing Sikasil® WT-488 both components have to be mixed homogeneously and air-bubble-free in the correct ratio as indicated with an accuracy of ±10 %. Most commercially available metering and mixing equipment are suitable. For advice on selecting and setting up a suitable pump system, contact the System Engineering Department of Sika Industry.
Consider that the B-component is moisture-sensitive and must therefore only be exposed briefly to air.
Joints must be properly dimensioned.
Basis for calculation of the necessary joint dimensions are the technical values of the adhesive and the adjacent building materials, the exposure of the building elements, their construction and size as well as external loads.
Tooling and finishing
Tooling and finishing must be carried out within the snap time of the adhesive.
When tooling freshly applied Sikasil® WT-488, press the adhesive to the joint flanks to get a good wetting of the bonding surface. No tooling agents must be used.
Removal
Uncured Sikasil® WT-488 may be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using a suitable industrial hand cleaner and water.
Do not use solvents on skin.
Overpainting
Sikasil® WT-488 cannot be overpainted.
Application Limits
To exclude materials influencing Sikasil® WT-488, all materials such as gaskets, setting blocks, sealants, etc., in direct and indirect contact have to be approved by Sika in advance.
Where two or more different reactive sealants are used, allow the first to cure completely before applying the next one.
The above mentioned Sika process materials may only be used in structural glazing or window bonding applications after a detailed examination and written approval of the corresponding project details by Sika Industry.