Sikaflex®-511
Sikaflex®-511 is a 1-component, high movement Silane Terminated Polymer (STP) textured sealant that cures on exposure to atmospheric humidity. It is well suited for applications that require both paintability and adhesion to non-porous substrates.
- Meets the requirements of ASTM C1248, ASTM C920 Type S, Grade NS, Class 50, Use M (w/ Sika® Primer-210), A, O-Vinyl
- Good weathering resistance
- Designed for porous and non-porous substrates
- Textured appearance blends well to rough or stucco type surfaces
- Isocyanate free
- Overpaintable with most paints
PRODUCT BENEFITS
- Meets the requirements of ASTM C1248, ASTM C920 Type S, Grade NS, Class 50, Use M (w/ Sika® Primer-210), A, O-Vinyl
- Good weathering resistance
- Designed for porous and non-porous substrates
- Textured appearance blends well to rough or stucco type surfaces
- Isocyanate free
- Overpaintable with most paints
Usage
Sikaflex®-511 can be used for joints or gaps connecting dissimilar substrates such as vinyl to concrete or aluminum to EIFS. Seek manufacturer’s advice and perform tests on original substrates before using Sikaflex®-511 on materials prone to stress cracking. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.Packaging
| Cartridge | 295 ml |
| Unipack | 600 ml |
Product Details
| Chemical base | Silane Terminated Polymer | |
| Color (CQP001-1) | White, aluminium grey, dark bronze, tan, anodized aluminum, stone, off-white, medium bronze, black, limestone, special bronze | |
| Cure mechanism | Moisture-curing | |
| Density (uncured) | 1.44 kg/l | |
| Non-sag properties | Very good | |
| Application temperature | ambient | 5 ─ 40 °C (41 ─ 104 °F) |
| Skin time (CQP019-1) | 70 minutes A | |
| Curing speed (CQP049-1) | See diagram 1 | |
| Shore A hardness (CQP023-1 / ISO 48-4) | 20 | |
| Tensile strength (ASTM D412) | 0.7 MPa (100 psi) | |
| Elongation at break (ASTM D412) | 300 % | |
| Tear propagation resistance (CQP045-1 / ISO 34) | 6 N/mm (35 pli) | |
| Service temperature (CQP513-1) | -40 ─ 77 °C (-40 ─ 170 °F) | |
| Shelf life (CQP016-1) | 12 months B |
| CQP = Corporate Quality Procedure | A) 23 °C (73 °F) / 50% r.h. | B) stored below 25 °C (77 °F) |
CURE MECHANISM
Sikaflex®-511 cures by reaction with atmospheric moisture. At low temperatures the water content of the air is generally lower and the curing reaction proceeds somewhat slower (see diagram 1).
Diagram 1: Curing speed of Sikaflex®-511
Application
Surface Preparation
Surfaces must be clean, dry and free from grease, oil, dust and contaminants.
Surface treatment depends on the specific nature of the substrates and is crucial for a long lasting bond. Suggestions for surface preparation may be found on the current edition of the appropriate Sika® Pre-Treatment Chart. Consider that these suggestions are based on experience and have in any case to be verified by tests on original substrates.
Application
Sikaflex®-511 can be processed between 5 °C and 40 °C (41 °F and 104 °F), climate and product, but changes in reactivity and application properties have to be considered. The optimum temperature for substrate and process material is between 15 °C and 25 °C (59 °F and 77 °F).
Sikaflex®-511 can be processed with manual, pneumatic or electric driven piston guns.
Tooling and finishing
Tooling and finishing must be carried out within the skin time of the product. It is recommended using Sika® Tooling Agent N. Other finishing agents must be tested for suitability and compatibility prior the use.
Removal
Uncured Sikaflex®-511 may be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using a suitable industrial hand cleaner and water. Do not use solvents on skin.
Overpainting
Sikaflex®-511 can be best painted within the skin formation time. If painting process takes place after the sealant has built a skin, adhesion could be improved by treating the joint surface with Sika® Aktivator-100 or Sika® Aktivator-205 prior to paint process. If the paint requires a baking process (> 80 °C (176 °F)), best performance is achieved by allowing the sealant to fully cure first. All paints have to be tested by carrying preliminary trials under manufacturing conditions.
The elasticity of paints is usually lower than that of sealants. This could lead to cracking of the paint in the joint area.
Application Limits
- Maximum depth of selant must not exceed 13 mm (1/2 in.); minmum depth is 6 mm (1/4 in.).
- Not intended for immersion, structural glazing applications, or horizontal vehicular traffic.
- Do not apply to damp or wet substrates.
- Allow treated wood to age six months before application.