Sikagard® H 400
(formerly MProtect H 400)
WATER-BASED 40% SILANE PENETRATING SEALER
0.0 (0)
Sikagard® H 400 is a water-based, 40% alkylalkoxysilane penetrating sealer. It provides long-lasting protection against moisture intrusion, freeze/thaw cycles, and chloride intrusion.
- Excellent penetration protecting against damage from moisture intrusion and chloride ion penetration
- 40% silane
- Ideal for traffic-bearing surfaces
- Breathable to allow interior moisture to escape without damaging sealer
- Does not alter the surface appearance
- One component for ease of application
Usage
- Interior or exterior
- Horizontal and vertical
- Above grade
- Parking garages
- Stadiums
- Bridge decks
- Concrete highway road surfaces
- Ramps and barrier rails
- Many other reinforced concrete structures
- Architectural
- Glass-fiber-reinforced
- Precast
- Cast in place
Advantages
- Excellent penetration protecting against damage from moisture intrusion and chloride ion penetration
- 40% silane
- Ideal for traffic-bearing surfaces
- Breathable to allow interior moisture to escape without damaging sealer
- Does not alter the surface appearance
- One component for ease of application
Packaging
5 gallon (19 L) pails
54 gallon (205 L) drums
Color
Milky white; dries clear
Product Details
APPROVALS / STANDARDS
Alberta DOT, Type 1b
Chemical Base
Sikagard® H 400 is a water-based alkylalkoxysilane sealer.
Active content
40%
Shelf Life
18 months when properly stored
Storage Conditions
Store in unopened containers in a clean, dry area between 35 °F and 110 °F (2 °C and 43 °C). Keep from freezing.
Density
7.9 lbs/gal
Specific gravity
0.95 at 77 °F (25 °C)
Flash Point
> 200 °F (> 93 °C) | (ASTM D 3278, SETA) |
Solid content by mass
40%
Penetration Depth
0.24 in (6.1 mm), average depth depending upon substrate
Water Absorption
48 Hours | 0.42% |
50 Days | 1.2% |
Water weight gain
85% reduction – exceeds criteria | (NCHRP 244 Series II-cube test) |
Water resistance
Initial performance | 89% |
Post-abrasion performance | 89.4% |
Freeze Thaw De-Icing Salt Resistance
non-air-entrained concrete, 100 cycles-treated concrete | 0 – No Scaling |
Test results are averages obtained at a coverage rate of 125 ft2/gal (3.12 m2/3.8 L) under laboratory conditions.
Reasonable variations can be expected.
Application
Drying Time
Typical drying time for Sikagard® H 400 is 4 hours at 70 °F (21 °C) and 50% relative humidity. Cooler temperatures or higher relative humidity can extend the drying time.
Coverage
Concrete:
- 100–200 ft2/gal (2.4–4.8 m2/L
Brick:
- 100–200 ft2/gal (2.4–4.8 m2/L)
Always apply a test area to determine actual coverage rates. Coverage rates will vary greatly with the porosity of the substrate.
APPLICATION INSTRUCTIONS
For Best Performance
- Keep material from freezing.
- Do not dilute Sikagard® H 400.
- Water repellents perform best when applied to a dry substrate, when power washing is performed, allow for a proper dry time before applying the water repellent.
- Do not apply during inclement weather or when inclement weather is anticipated within 12 hours.
- To prevent damage to nearby shrubbery and landscaping, cover or protect with drop cloth.
- Protect asphalt-based products such as roofing materials or plastic products from overspray.
- Sikagard® H 400 may leave a temporary slippery surface for up to several hours after application. Therefore, traffic-bearing surfaces should not be reopened until the treated surface is dry.
- Variations in the texture and porosity of the substrate will affect the coverage and performance of the product.
- Sikagard® H 400 will not inhibit water penetration through unsound or cracked surfaces or surfaces with defective flashing, caulking, or structural waterproofing.
- Line striping can be done after the application of the sealer.
- Make certain the most current versions of the product data sheet and SDS are being used.
- Proper application is the responsibility of the user. Field visits by Sika personnel are for the purpose of making technical recommendations only and are not for supervising or providing quality control on the jobsite.
SUBSTRATE PREPARATION
- Verify substrate has properly cured. Concrete should obtain 80% of design strength, typically achieved within 14–28 days.
- Clean concrete surfaces of all sand, surface dust and dirt, oil, grease, chemical films, coatings, and other contaminants prior to application. Power wash, sandblast, or shotblast as necessary to achieve the desired surface condition.
- Surface, air, and material temperatures should be 40 to 110 °F (4 to 43 °C) during application. Do not apply Sikagard® H 400 when temperatures are expected to fall below 40 °F (4 °C) within 12 hours.
- A dry surface is suggested for maximum penetration of sealer; however, surfaces to be treated can be slightly damp.,. Do not apply Sikagard® H 400 if standing water is visible on the surface to be treated.
- Crack control, caulking, patching, and expansion joint sealants can be installed before or after the application of the sealer. Allow a minimum of 6–12 hours of curing time for caulking and sealant materials (or until they have skinned over) before applying Sikagard® H 400. Following the application, remove the excess product that might pond on a concave sealant joint.
APPLICATION
- Test a small area of the surface (generally a 5 by 5 ft [1.5 by 1.5 m] section) before starting the general application of any clear penetrating sealer to ensure desired performance results, aesthetics, and coverage rates. Allow 5–7 days for the product to fully react before evaluation.
- Stir material thoroughly before and during application.
- Apply to saturation. Apply by low-pressure non-atomizing spray or, if desired on horizontal surfaces, by pouring, followed by a squeegee or a broom for even distribution.
CLEANING OF TOOLS
Clean equipment and tools with hot soapy water. Overspray can be cleaned immediately with hot soapy water. Dried residue can be cleaned with a mild citrus-based cleaner or very hot water, then scrubbed with a soft-bristle brush.