Sikadur®-42 Grout-Pak
Pre-proportioned, epoxy, baseplate grouting system
0.0 (0)
Sikadur®-42 Grout-Pak is a 3-component, 100 % solids, moisture-tolerant, epoxy baseplate grouting system.
- Ready to mix, pre-proportioned kit
- Moisture-tolerant
- Corrosion and impact resistant
- Stress and chemical resistant
- Long working time
- High vibration resistance
- Fast strength gain
- Low peak exothermic system for large pours
- High effective bearing area
- Excellent flowability
- USDA certifiable for incidental food contact
Usage
- Precision seating of baseplates
- Precision grouting of wind turbine tower bases requiring rapid strength gain
- Grouting under equipment, including heavy impact and vibratory machinery, reciprocating engines, compressors, pumps, presses, etc.
- Grouting for “pour-back” anchorage on post tensioning projects (e.g. segmental bridge)
- Grouting under crane rails
Advantages
- Ready to mix, pre-proportioned kit
- Moisture-tolerant
- Corrosion and impact resistant
- Stress and chemical resistant
- Long working time
- High vibration resistance
- Fast strength gain
- Low peak exothermic system for large pours
- High effective bearing area
- Excellent flowability
- USDA certifiable for incidental food contact
Packaging
0.5 ft3 kit: Contains 0.9 gal. epoxy (Component A in 2 gal pail and Component B in a 2 gal. pail), and 50 lb. aggregate (Component C) in a multi-wall bag.
1.5 ft3 kit: Contains 2.7 gal. epoxy (Component A in a 5 gal. (19 L) pail and Component B in a 2 gal. pail) and 150 lb. aggregate (Component C) in three 50 lb. multi-wall bags.
Color
Concrete gray
Product Details
Shelf Life
24 months from date of production if stored properly in original, unopened and undamaged sealed packaging
Storage Conditions
Store dry at 40–95 °F (4–35 °C).
Protect from moisture. If damp, discard material.
Compressive Strength
| 40 °F* (4 °C) | 73 °F* (23 °C) | 90°F* (32 °C) | |
| 8 hour | - | - | 5,500 psi (37.9 MPa) |
| 16 hour | - | 9,600 psi (66.2 MPa) | 9,800 psi (67.6 MPa) |
| 1 day | - | 12,200 psi (84.1 MPa) | 11,500 psi (79.3 MPa) |
| 3 days | 4,800 psi (33.1 MPa) | 14,000 psi (96.6 MPa) | 14,000 psi (96.6 MPa) |
| 7 days | 13,700 psi (94.5 MPa) | 14,900 psi (102.8 MPa) | 14,800 psi (102.1 MPa) |
| 14 days | 13,900 psi (95.9 MPa) | 15,000 psi (103.4 MPa) | 15,200 psi (104.8 MPa) |
| 28 days | 13,900 psi (95.9 MPa) | 15,200 psi (104.8 MPa) | 15,600 psi (107.6 MPa) |
* Material cured and tested at the temperatures indicated
Effective Bearing Area
> 95 %*
* Percent final surface area of grout in contact with bearing plate
Flexural Strength
| 4,000 psi (27.6 MPa) (7 days) | (ASTM C-580) 73 °F (23 °C) |
Modulus of Elasticity in Flexure
| 1.30 x 106 psi (8,963 MPa) (7 days) | (ASTM C-580) 73 °F (23 °C) 50 % R.H. |
Tensile Strength
| 2,300 psi (15.8 MPa) (7 days) | (ASTM C-307) 73 °F (23 °C) 50 % R.H. |
Tensile Adhesion Strength
| Bond Strength to Concrete, 4,200 psi (29.0 MPa) (7 days) | (ASTM C-882 modified) 73 °F (23 °C) 50 % R.H. |
Thermal Compatibility
| passes test | (ASTM C-884) |
Coefficient of Thermal Expansion
| 24.5 x 10-6 in./in./ °F (13.7x10-6 mm/mm/ °C) | (ASTM C-531) |
Water Absorption
| 0.04 % (2-hour boil) | (ASTM C-413) |
Application
Product Temperature
41–86 °F (5–30 °C)
Substrate Temperature
41–86 °F (5–30 °C)
Pot Life
Approximately 90 minutes
SUBSTRATE PREPARATION
Substrate and baseplate contact area must be clean, sound, and free of standing water. Remove dust, laitance, oils, grease, curing compounds, waxes, impregnations, foreign particles, coatings and disintegrated materials by mechanical means (i.e., sandblasting, bush hammering). Sandblast metal baseplates to a commercial white finish for maximum adhesion. Apply grout immediately to prevent re-oxidizing. Concrete substrate must have reached its desired strength (3,000 psi minimum) and must be dimensionally stable.
MIXING
0.5 ft3 kit: Pour the entire contents of Components A & B into an appropriate mixing vessel (e.g. 5 gal.) bucket) and mix for 30 seconds with a 1/2 in. Jiffy mixing paddle (5 in. blade diameter) on a low-speed (400–600 rpm) 3/4 in. drive rotary drill, taking care not to entrain air during mixing. Do not over-mix. It is critical to the performance of the grout that there be no appreciable air bubbles in the resin. Slowly add the entire contents of Component C and mix until uniformly blended (approx. 5 minutes).
1.5 ft3 kit: Pour the entire contents of Components A & B into an appropriate mixing vessel (e.g. 5 gal. bucket) and mix for 30 seconds with a 1/2 in. Jiffy mixing paddle (5 in. blade diameter) on a low-speed (400– 600 rpm) 3/4 in. drive rotary drill, taking care not to entrain air during mixing. Do not over-mix. It is critical to the performance of the grout that there be no appreciable air bubbles in the resin. Transfer the mixed resin to an appropriate mixing vessel. Slowly add the entire 3 bags of Component ‘C’ and mix until uniformly blended (approx. 5 minutes).