Product Data Sheet Show all documents
SikaEmaco®-1060 EX

SikaEmaco®-1060 EX

(formerly MEmaco T 1060EX)

LOW-DUST, VERY RAPID-SETTING CEMENT-BASED PRE-EXTENDED CONCRETE REPAIR MORTAR

SikaEmaco®-1060 EX is a one-component, shrinkage-compensated, very rapid-setting, cement-based pre-extended mortar. It is designed for repairing horizontal concrete surfaces where high early strength gain is required in applications from 1.5" (38 mm) to full depth.

  • Pre-extension with coarse aggregate at the factory ensures quality and saves contractor labor
  • Low-dusting for added worker comfort and safety
  • Extra low permeability helps minimize chloride intrusion
  • Very rapid setting so that structures can be opened to vehicular traffic in 1 hour
  • Low residual moisture, can be coated in as little as 4 hours
  • Excellent freeze/thaw cycling
  • Shrinkage-compensated, to minimize cracking from drying shrinkage, which reduces stress at the bond line
  • Proprietary cement blend bonds to carbonated and noncarbonated concrete substrates
Product Data Sheet Show all documents

Usage

  • Interior and exterior
  • Horizontal surfaces
  • Applications requiring high early strength gain
  • Structural concrete repairs
  • Partial and full-depth repairs
Substrates
  • Concrete
 

Advantages

  • Pre-extension with coarse aggregate at the factory ensures quality and saves contractor labor
  • Low-dusting for added worker comfort and safety
  • Extra low permeability helps minimize chloride intrusion
  • Very rapid setting so that structures can be opened to vehicular traffic in 1 hour
  • Low residual moisture, can be coated in as little as 4 hours
  • Excellent freeze/thaw cycling
  • Shrinkage-compensated, to minimize cracking from drying shrinkage, which reduces stress at the bond line
  • Proprietary cement blend bonds to carbonated and noncarbonated concrete substrates

Packaging

50 lb (22.6 kg) polyethylene-lined bags

Product Details

Product Information

Chemical Base

SikaEmaco®-1060 EX is a blend of cement, graded aggregate, shrinkage-compensating agents, and set-control additives.

Shelf Life

1 year when properly stored

Storage Conditions

Store in unopened containers in cool, clean, dry conditions.
Technical Information

Compressive Strength

2" Cubes

1 hr: 2,000psi (14MPa)

1 day: 4,000psi (28MPa)

28 days: 8,000psi (55MPa)

3 by 6" cylinders

28 days: 7,400psi (51MPa)

Modulus of Elasticity in Compression

6.07 x 106psi

(ASTM C 469)

Flexural Strength

1 day: 715psi (5MPa)

28 days: 1,060psi (7MPa)

Splitting tensile strength

1 day: 485psi (3MPa)

28 days: 555psi (4MPa)

(ASTM C 496)

Shear Strength

Slant shear bond strength

1 day: 2,500psi (17MPa)

28 days: 2,900psi (20MPa)

Shrinkage

Drying Shrinkage

-0.04% (-400μstrain)

Expansion

Wetting expansion+0.02% (+200μstrain)

(ASTM C 928)

Coefficient of Thermal Expansion

7.3 x 10-6in/in/°F (13.4 x 10-6cm/cm/°C)

(CRD C 39)

Freeze-Thaw Stability

92.6% RDM at 300 cycles

Freeze Thaw De-Icing Salt Resistance

Scaling resistance

0 rating(no scaling) at 25 cycles

(ASTM C 672)

Design Considerations

Dust reduction

SikaEmaco®-1060 EX vs control: 70% 

Application

Application Information

Fresh mortar density

148lb/ft3 (2,370kg/m3) 

Flowability

Slump

3-5in (8-13cm)

Ambient Air Temperature

Application temperature range40-85°F (4-29°C)

Thinner

Working time

8 min

Set Time

16 min at 72°F (22°C)

Final set time

28 min at 72°F (22°C)

(ASTM C 191)
Consumption

Coverage

0.38 ft³ (0.010 m³) per 50 lb (22.6 kg) bag
Application steps

NOTES ON INSTALLATION

  • Minimum ambient, surface, and material temperature is 40 °F (4 °C) and rising.
  • Do not mix for longer than 5 minutes.
  • Minimum application thickness is 1.5" (38 mm).
  • Consult coating supplier for overcoating requirements.
  • Do not mix partial bags.
  • Do not add plasticizers, accelerators, retarders, or other additives.
  • For professional use only; not for sale to or use by the general public.
  • Make certain the most current versions of the product data sheet and SDS are being used.
  • Proper application is the responsibility of the user. Field visits by Sika personnel are for the purpose of making technical recommendations only and are not for supervising or providing quality control on the jobsite

SURFACE PREPARATION

Concrete

  1. Concrete must be structurally sound and fully cured (28 days).
  2. Saw cut the perimeter of the area being repaired into a square with a minimum depth of 1/2" (13 mm).
  3. Refer to current ICRI Guideline no. 310.2R for surface prep requirements to permit proper bond.

Reinforcing steel

  1. Remove all oxidation and scale from the exposed reinforcing steel in accordance with ICRI Technical Guideline No. 310.1R.
  2. For additional protection from future corrosion, coat the prepared reinforcing steel with Sikagard® P 8100 AP.

MIXING

  1. Precondition material to 70 °F ±5° (21 °C ±3°) before mixing.
  2. Add 3.25 pints (1.5 L) of potable water to the mixing container for each bag of SikaEmaco®-1060 EX. Add the powder to the water while continuously mixing with a slow-speed drill and paddle, mortar mixer, or other forced action mixer.
  3. Mix for a minimum of 3 minutes until fully homogeneous.

 

APPLICATION

  1. After removing all standing water, thoroughly scrub a thin layer of bond coat into the saturated surface with a stiff-bristled broom or brush. Do not dilute the bond coat with water. Do not apply more of this bond coat than can be covered with mortar before the bond coat dries. Do not retemper the bond coat.
  2. Immediately place the repair mortar from one side of the prepared area to the other. Work the material firmly into the bottom and sides of the patch to ensure a good bond. Level the SikaEmaco®-1060 EX and screed it to the elevation of the existing concrete. Apply the appropriate finish.
  3. Finish the completed repair, as required, taking care not to overwork the surface.
  4. The recommended application range of SikaEmaco®-1060 EX is from 40 to 85 °F(4 to 29 °C). Follow ACI 305 and 306 for hot or cold weather.

CURING TREATMENT

Cure with an approved curing compound compliant with ASTM C 309 or preferably ASTM C 1315. Alternative curing options include the application of a fine mist of water, wet burlap, or polyethylene sheeting for a minimum of 2 days.

CLEANING OF TOOLS

Clean tools and equipment with clean water immediately after use. Cured material must be removed mechanically.