Product Data Sheet
Show all documents
Sikadur®-22 Lo-Mod LT

Sikadur®-22 Lo-Mod LT

Low-modulus, fast-setting, medium viscosity, urethane modified, epoxy resin binder for low-temperature applications

Sikadur 22, Lo-Mod LT is a 2-component, 100% solids, moisture-tolerant, urethane modified, epoxy binder capable of curing quickly at temperatures below 50F. It conforms to the current ASTM C-881* Type III, Grade 2, Class B & C and AASHTO M-235 specifications. * Except Gel Time

  • Fast setting for quick turn around
  • Meets 3 hr/1000 psi requirement when mixed as an epoxy mortar
  • Tolerant to moisture both before and after cure
  • Convenient easy mix ratio A:B = 1:1 by volume
  • Excellent strength development
  • Leveling viscosity for easy, efficient application of a broadcast overlay
  • Tack-free in 3.5 hours at 50°F (10°C)
  • Can condition material at elevated temperatures for faster cure rates
Product Data Sheet
Show all documents

Usage

Use neat as the binder resin for a skid-resistant broadcast overlay. Use also as the binder resin for epoxy
mortar and concrete for patching and overlays.  

Advantages

  • Fast setting for quick turn around
  • Meets 3 hr/1000 psi requirement when mixed as an epoxy mortar
  • Tolerant to moisture both before and after cure
  • Convenient easy mix ratio A:B = 1:1 by volume
  • Excellent strength development
  • Leveling viscosity for easy, efficient application of a broadcast overlay
  • Tack-free in 3.5 hours at 50°F (10°C)
  • Can condition material at elevated temperatures for faster cure rates

Packaging

4 gal., 110 gallon, 660 gallon totes.

Note: Part A of the Sikadur 22 Lo-Mod, Sikadur 22 Lo-Mod FS, Sikadur 22 Lo-Mod LT and Sikadur 21 Lo-Mod LV is a universal component of these four products.

Color

amber

Product Details

Product Information

Chemical Base

epoxy resin

Shelf Life

2 years in original, unopened containers

Storage Conditions

Store dry at 40°-95°F (4°-35°C). Condition material to 65°-85°F (18°-29°C) before using.

Viscosity

1,300-1,500 cps
Technical Information

Shore D Hardness

78

(ASTM D2240)

Compressive Strength

Time

40°F

73°F

3 hrs

>1,500 psi

>5,000 psi

24 hrs

>5,000 psi

>7,000 psi

7 days>8,000 psi>8,000 psi

Tensile Strength

7 days

>3,000 psi

Tensile Adhesion Strength

24 hrs

>250 psi (substrate failure)

Water Absorption

7 days

<0.15%

Application

Application Information

Mixing Ratio

Comp. "A": Comp. "B" = 1:1 by volume

Contact time

Gel Time (60g)

10 min

Cure Time

Substrate Temperature

Tack Free Time

40°F

<3 hrs

50°F

<2 hrs

73°F~1 hr
Consumption

Coverage

1 gal. yields 231 in3

For traffic overlay - 1 gal yields ~32 ft2

Mortar Binder - 1 gal. of mixed Sikadur® 22 Lo-Mod LT with the addition of 5 gal. by loose volume of an oven dried sand, yields approximately 808 cu. in. of epoxy mortar.
Application steps

SUBSTRATE PREPARATION

Surface must be clean and sound. It may be dry or damp, but free of standing water. Remove dust, laitance, grease, curing compounds, impregnations, waxes and any other contaminants.

Concrete - Should be cleaned and prepared to achieve a laitance and contaminant free, open textured surface by blast cleaning or equivalent mechanical means.

Steel - Should be cleaned and prepared thoroughly by blast cleaning to white metal finish.

MIXING

Pre-mix each component. Proportion equal parts by volume of Component ‘A’ and ‘B’ into clean pail. Mix thoroughly for 3 min. with Sika paddle on low-speed (400-600 rpm) drill until uniformly blended. Mix only that quantity that can be used within pot life.

To prepare epoxy mortar - Slowly add 5 parts by loose volume of oven-dried sand to 1 part mixed resin

Documents