Show all documents

Sikaflex® Self Leveling Sealant

High performance, self-leveling,1-part polyurethane sealant

Sikaflex® Self Leveling Sealant is a single component, self-leveling, premium-grade polyurethane sealant with an accelerated curing capacity. Meets Federal Specification TT-S-00230C, Type 1, Class A. Meets ASTM C-920, Type S, Grade P, Class 25.

  • 1-component, no mixing
  • Self-leveling, pourable
  • Accelerated curing
  • Permanently elastic
  • High durability
  • Resists aging, weathering
  • Excellent adhesion
  • Convenient, easy-to-use packaging
  • Paintable with water-based, oil-based or rubber-based paints
Show all documents

Usage

Sikaflex® Self Leveling Sealant is used to seal horizontal expansion joints in concrete and cementitious slabs such as:
  • Driveways
  • Garages
  • Sidewalks
  • Balconies
  • Pavements
  • Terraces
  • Warehouses
  • Factories
  • Civil Structures
  • Plazas
 

Advantages

  • 1-component, no mixing
  • Self-leveling, pourable
  • Accelerated curing
  • Permanently elastic
  • High durability
  • Resists aging, weathering
  • Excellent adhesion
  • Convenient, easy-to-use packaging
  • Paintable with water-based, oil-based or rubber-based paints

Packaging

10.1 fl. (299 ml) oz. moisture proof composite cartridge, 12/case

29 fl. oz. (858 ml) moisture-proof composite cartridges, 12/case

Color

Gray in 10.1 fl. oz. (299 ml) and 29 fl. oz. (858 ml) cartridges.

Sandstone in only 29 fl. oz. (858 ml) cartridge

Product Details

Product Information

Shelf Life

12 months in original unopened packaging

Storage Conditions

Store at 40 to 95 °F (4 to 35 °C). Condition material to 65 to 75 °F (18 to 24 °C) before using
Technical Information

Shore A Hardness

40 ± 5 (21 days)

(ASTM D-2240)

Tested at:

73 °F (23 °C)
50 % R.H.)

Tensile Strength

150 psi (1 MPa) (21 days)

(ASTM D-412)

Tested at:

73 °F (23 °C)
50 % R.H.

Tensile Stress at Specified Elongation

110 psi at 100% (0.7 MPa) (21 days)

(ASTM D-412)

Tested at:

73 °F (23 °C)
50 % R.H.

Elastic Recovery

> 90 %

Adhesion in Peel

Substrate

Peel Strength

Adhesion Loss

Concrete

> 30 pli

0 % Adhesion Loss

Movement Capability

± 25 %

Resistance to Weathering

Excellent

Service Temperature

-40 to 170 °F (-40 to 76 °C)

Application

Application Information

Ambient Air Temperature

40 to 100 °F (4 to 38 °C). Sealant should be installed when joint is at midrange of its anticipated movement

Substrate Temperature

40 to 100 °F (4 to 38 °C). Sealant should be installed when joint is at midrange of its anticipated movement

Cure Time

Final Cure: 3 to 5 days

Tack Free Time

1 to 2 hours
Consumption

Coverage

10.1 oz (299 ml) Cartridge: Yield in Linear Feet

1/4" Depth

3/8" Depth

1/2" Depth

Width

1/4"

24.3

3/8"

16.2

10.8

1/2"12.18.16.1
3/4"8.1  5.44.0
1"3.0
1-1/4"2.4
1-1/2"2.0

29 oz (858 ml) Cartridge: Yield in Linear Feet

1/4" Depth3/8" Depth1/2" Depth
Width
1/4"69.8
3/8"46.531.0
1/2"34.923.317.4
3/4"23.215.511.6
1"8.7
1-1/4"7.0
1-1/2"5.8
 
Application steps

SUBSTRATE PREPARATION

Clean all surfaces. Joint walls must be sound, clean, dry, frost-free, and free of oil and grease. Curing compound residues and any other foreign matter must be thoroughly removed. Install bond breaker tape or backer rod to prevent bond at base of joint.

   

Priming is not usually necessary. Substrates only require priming if testing indicates a need. Consult Sikaflex Primer Technical Data Sheet or Technical Service for additional information on priming.

 

Documents