Sika® Ucrete® UD 200
(formerly Ucrete® UD 200)
Hygienic, slip-resistant, heavy-duty polyurethane floor screed
0.0 (0)
Sika® Ucrete® UD 200 is a lightly textured, heavy-duty resin floor with very good resistance to aggressive chemicals, heavy impact and temperatures up to 302°F (150°C).
- Expert installation by fully trained applicators
- Does not support bacterial or mold growth
- Suitable for application on to 7-day-old concrete and 3-day-old polymer screed
- Can be accelerated with Sika® Ucrete® Accelerator for fast installation within a 12-hour window
- Very good resistance to a wide range of chemicals
- Very good mechanical resistance
- Impermeable to liquids
- Non-tainting from the end of mixing
- Low VOC emissions
- Thermal expansion properties similar to concrete
- Tolerant to substrates with high moisture content
Usage
Sika® Ucrete® UD 200 is used as a wearing layer screed for Sika® Ucrete® flooring systems. Sika® Ucrete® UD 200 is used within wet and dry process areas including the following application areas:- Food and beverage facilities
- Pharmaceutical facilities
- Chemical and processing facilities
- Manufacturing facilities and workshops
- The Product may only be used by experienced professionals.
Advantages
- Expert installation by fully trained applicators
- Does not support bacterial or mold growth
- Suitable for application on to 7-day-old concrete and 3-day-old polymer screed
- Can be accelerated with Sika® Ucrete® Accelerator for fast installation within a 12-hour window
- Very good resistance to a wide range of chemicals
- Very good mechanical resistance
- Impermeable to liquids
- Non-tainting from the end of mixing
- Low VOC emissions
- Thermal expansion properties similar to concrete
- Tolerant to substrates with high moisture content
Packaging
Refer to the current price list for available packaging variations.
Color
| Cured color | Red, Orange, Yellow, Cream, Grey, Light Grey, Green, Light Green, Green/ Brown, Blue. |
Product Details
APPROVALS / STANDARDS
Halal Certification Europe (HCE), Sika® Ucrete®, WHFC, Certificate No. 21453-2/1/1/Y1
Food and Beverage Facilities Suitability, Sika® Ucrete®, HACCP, Test Report No. I-PE-769-SA-2-RG-06b
Indoor Air Comfort Gold EN 16516, Sika® Ucrete®, eurofins, Certificate No. IACG-321-01-01-2023
Chemical Base
Water-based polyurethane cement hybrid
Shelf Life
Always refer to the best-before date of the individual packaging.
Storage Conditions
The Product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between 40°F and 85°F. Always refer to the packaging.
Refer to the current Safety Data Sheet for information on safe handling and storage.
Density
| Mixed Product | 130.47 lb/ft3 |
Compressive Strength
| Cured 28 days at 73°F | 7977 psi |
Modulus of Elasticity in Compression
3250 MPa | (BS 6319-6) |
Flexural Strength
| Cured 28 days at 73°F | 2030 psi |
Tensile Strength
| Cured for 28 days at 68°F | 845 psi |
Tensile Adhesion Strength
| >290 psi (concrete failure) | (ASTM D4541) |
Coefficient of Thermal Expansion
| 2.2 × 10-5 °F-1 | (ASTM C531) |
Service Temperature
| Thickness | Minimum | Maximum | Occasional spillage |
| 1/4 in | -13 °F | 176 °F | - |
| 3/8 in | -40 °F | 248 °F | - |
| 1/2 in | -40 °F | 266 °F | 302 °F |
Chemical Resistance
Laboratory-defined resistance to many individual chemicals. Before proceeding, contact Sika Technical Service for specific information.
Reaction to Fire
Class Bfl-s1 | (EN 13501-1) |
Application
Layer Thickness
~1/4 - 1/2 in
Product Temperature
| Maximum | 86 °F |
| Minimum | 50 °F |
Ambient Air Temperature
| Maximum | 95 °F |
| Minimum | 41 °F |
Substrate Temperature
| Maximum | 86 °F |
| Minimum | 41 °F |
Cure Time
| Substrate temperature | Return to traffic |
| 46 °F | < 24 hours |
| 50 °F | 4 hours (with Sika® Ucrete® Accelerator) |
Note: Times are approximate and will be affected by changing ambient and substrate conditions.
Coverage
| Layer | Product | Coverage Rate |
| Wearing layer | Sika® Ucrete® UD 200 | 22 ft2/kit for 1/4 in 16 ft2/kit for 3/8 in 11 ft2/kit for 1/2 in |
SUBSTRATE PREPARATION
IMPORTANT
Reduced service life due to incorrect treatment of cracks
The incorrect assessment and treatment of cracks may lead to a reduced service life and reflective cracking.
- For static cracks, ensure the width is suitable for overcoating with Sika® Ucrete® UD 200.
- For dynamic cracks, ensure the movement is within the movement capacity of Sika® Ucrete® UD 200.
TREATMENT OF JOINTS AND CRACKS
Construction joints and existing static surface cracks in substrate require pre-treating before full layer application. Use Sikadur® or Sikafloor® resins.
The System can be applied on green or damp concrete with no standing water. Allow for at least 3 days for early concrete shrinkage to occur to prevent shrinkage cracks from appearing on the wearing surface.
Cementitious substrates must be structurally sound and of sufficient compressive strength (minimum 3625 psi, 25 N/mm2) with a minimum tensile strength of 217 psi.
Substrates must be clean, dry and free of contaminants such as dirt, oil, grease, coatings, laitance, surface treatments and loose friable material.
APPLICATION
Application must be undertaken by a fully trained Sika® Ucrete® applicator.