Sikalastic®-621 TC

Sikalastic®-621 TC

Single component saturating resin for Sikalastic® RoofPro systems

Sikalastic®-621 TC is a cold applied, highly elastic, aliphatic, single component, moisture triggered polyurethane resin designed for easy application as part of Sikalastic® -621 RoofPro systems.

  • Proven technology - over 30 year track record
  • Single component – no mixing and ready to use
  • Fully reinforced with highly conformable Sika Reemat or Sika Fleece
  • Moisture triggered chemistry that is rapidly weatherproof after application
  • Resistant to ponding water
  • UV resistant - Highly reflective and resistant to yellowing
  • Cold applied - requires no heat or flame
  • Seamless roofing/waterproofing membrane
  • Compatible with Sika® Reemat Premium - easy to detail
  • Fast curing - free from resin damage almost immediately on application
  • High elastic and crack bridging - retains flexibility even at low temperatures
  • Root resistant
  • Easily recoated renewable system - no stripping required
  • Good adhesion to most substrates- see primer chart
  • Vapor permeable - allows substrate to breathe
  • Strong resistance to common atmospheric chemicals
Product Data Sheet Safety Data Sheet Show all documents

Usage

  • Embedment and top coat resin for Sikalastic® RoofPro 10, 15, 20 & 25 year systems reinforced with Sika Reemat
  • Saturating resin for Sikalastic® RoofPro 15, 20 and 25 year systems reinforced with Sika Fleece
  • Typically applied in Sikalastic® RoofPro Direct, Recover, Built-Up, Inverted, and Vegetated systems for both new construction and refurbishment

Advantages

  • Proven technology - over 30 year track record
  • Single component – no mixing and ready to use
  • Fully reinforced with highly conformable Sika Reemat or Sika Fleece
  • Moisture triggered chemistry that is rapidly weatherproof after application
  • Resistant to ponding water
  • UV resistant - Highly reflective and resistant to yellowing
  • Cold applied - requires no heat or flame
  • Seamless roofing/waterproofing membrane
  • Compatible with Sika® Reemat Premium - easy to detail
  • Fast curing - free from resin damage almost immediately on application
  • High elastic and crack bridging - retains flexibility even at low temperatures
  • Root resistant
  • Easily recoated renewable system - no stripping required
  • Good adhesion to most substrates- see primer chart
  • Vapor permeable - allows substrate to breathe
  • Strong resistance to common atmospheric chemicals

Packaging

5 gal. (19 L) pail

Color

White, Pearl Gray, Steel Gray,  - Mushroom, and Custom Colors available with minimum order quantity

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • FM Approval Standard 4470 for Class 1 Roof Covers
  • ASTM E-108
  • ASTM D 6083
  • Miami Dade
  • Florida Building Code
Product Information

Chemical Base

Moisture triggered polyurethane

Shelf Life

9 months

Storage Conditions

Store dry between 35 °F and 77 °F (2–25 °C). Condition material to 50–77 °F (10–25 °C) before using for ease of application

Density

~12 lb./gal. (~1.44 kg/l) (73 °F, 23 °C)

Solid content by volume

81 %

(ASTM D-2697)

Volatile organic compound (VOC) content

183 g/l

(ASTM D-2369-81)
System information

System Structure

Please refer to Sikalastic®-601/621 System Data Sheet
Technical Information

Resistance to Static Puncture

(ASTM D-5602)

Tensile Strength

738 psi

(ASTM D-412)

Tear Strength

72 lbf/in

(ASTM D-624)

Solar Reflectance

0.87*

(ASTM C-1549)

*All values refer to the initial (properly cured, non-weathered) status of Sikalastic®-621 TC white

Solar Reflectance Index

≥ 108*

(ASTM 1980)

*All values refer to the initial (properly cured, non-weathered) status of Sikalastic®-621 TC white

Service Temperature

-22 °F (30 °C) min. / 176 °F (80 °C) max.

Chemical Resistance

Strong resistance to a wide range of reagents including paraffin, petrol, fuel oil, white spirit, acid rain, detergents and moderate solutions of acids and alkalis. Some low molecular weight alcohols can soften the material. Contact Sika technical service for specific information.

External Fire Performance

Class A

(ASTM E 108)

Application

Application Information

Ambient Air Temperature

41 °F (5 °C) min. / 95 °F (35 °C) max.

Relative Air Humidity

 80 % R.H. max.

Dew Point

Beware of condensation.

The substrate and uncured coating must be ≥ 5 °F (3 °C) above dew point.

Substrate Temperature

41 °F (5 °C) min. / 140 °F (60 °C) max.
 

Substrate Moisture Content

≤4 % moisture content. Test method: Sika®-Tramex meter
No rising moisture according to ASTM (Polyethylene-sheet)

Pot Life

Sikalastic®-621 TC is designed for fast curing. High temperatures combined with high air humidity will increase the curing process. Material in opened containers should be applied immediately. In opened containers, the material will form a film after 1 hour approx. (75 °F, 24 °C / 50 % R.H.).

Waiting / Recoat Times

Ambient conditions

Minimum waiting time overcoating

+40 °F / 50 % r.h.

14 hours

+50 °F / 50 % r.h.

  6 hours

+70 °F / 50 % r.h.  5 hours

 *After 7 days the surface must be cleaned and primed with Sika® Reactivation Primer before continuing.
Note: Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.

Applied Product Ready for Use

Ambient conditions

Rain resistant

Touch dry

Full cure

+40 °F / 50 % r.h.

10 min.

12 hours

24 hours

+50 °F / 50 % r.h.

10 min.

  6 hours

18–24 hours

+70 °F / 50 % r.h.

10 min.

  4 hours

12–18 hours


Note: Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Consumption

Coverage

Sika Reemat

Sika Fleece

80 sf/gal.–20 mils wet film thickness

25 sf/gal.–65 mils wet film thickness

53 sf/gal.–30 mils wet film thickness

20 sf/gal.–80 mils wet film thickness

45 sf/gal.–35 mils wet film thickness16 sf/gal.–100 mils wet film thickness
35 sf/gal.–45 mils wet film thickness-
Application steps

SUBSTRATE PREPARATION

All substrate surfaces shall be clean, dry and sound. Acceptable substrates include: sound concrete and cementitious screed, metals, wood, modified bitumen, mineralized felt, EPDM, hypalon, TPO, sprayed polyurethane foam, brick and stone, slate and tile, and existing liquid applied membranes. Reference separate System Data Sheet for specific surface preparation requirements.
 

Primer
Apply primer of a type suitable for the substrate. Allow primer to cure completely before applying Sikalastic®-621 TC resin. Reference separate System Data Sheet for specific primer recommendations.

MIXING

No mixing necessary

APPLICATION

Sika Reemat - Base Resin
Apply Sikalastic®-621 TC resin to the primed substrate surface by means of 1/2” (12.7 mm) nap phenolic resin core roller or brush at the specified application rate to achieve a uniform and consistent wet mil thickness (reference separate System Data Sheet). Material can also be squeegee or spray applied, in which case it should also be backrolled. Apply Sika Reemat into the wet embedment resin and roll the scrim to achieve full saturation and embedment. Reemat shall be torn/cut to conform to substrate transitions and flashing conditions, with a typical 2” (50.8 mm) reinforcement overlap. Resin shall saturate the Reemat from below. Apply additional Sikalastic®-621 TC resin as required to ensure full scrim embedment. Allow to cure completely before applying subsequent resin layers.

  

Sika Reemat - Intermediate and Top Resin
Apply Sikalastic®-621 TC resin to the cured Sikalastic® Reemat base layer by means of 1/2” (12.7 mm) nap phenolic resin core roller or brush at the specified application rate to achieve a uniform and consistent wet mil thickness (reference separate System Data Sheet). Material can also be squeegee or spray applied, in which case it should also be backrolled. Allow to cure completely before applying any subsequent resin layer, if specified.

  

Sika Fleece
Apply Sikalastic®-621 TC resin to the primed substrate surface by means of 1/2” (12.7 mm) nap phenolic resin core roller or brush to achieve a uniform and consistent thickness, applying approximately 2/3 of the resin required to achieve the specified application rate (reference separate System Data Sheet). Apply Sika Fleece into the wet embedment resin and roll the fleece to achieve partial saturation and full embedment. Fleece shall be cut to conform to substrate transitions and flashing conditions, with typical 3” (76.2 mm) side and 6” (152.4 mm) end reinforcement overlaps. Resin shall saturate the Fleece from below. Apply remaining 1/3 of the specified resin quantity to to ensure full fleece saturation and an even resin application.

CLEANING OF TOOLS

Clean all tools and application equipment with appropriate solvent immediately after use. Hardened and/or cured material can only be removed mechanically
 

 